Abrasion Resistant Steel Plate Grade 600

Chemical CompositionGRADEBRANDORIGINChemical CompositionCSiMnCrMoBOTHERS(%)GR 600BISPLATE 600Australia0.450.350.401.200.300.002P 0.020ABREX 600Japan0.450.702.001.200.600.005P 0.015HARDOX 600Sweden0.400.801.501.500.500.005P 0.025XAR 600Germany0.450.701.001.200.800.004P 0.015Mechaniacal PropertiesGRADEBRANDORIGINYeild Point(N/mm²)Tensile Strength(N/mm²)Elongation(%)Impact ValueHardness BeurinnelGR 600BISPLATE 600Australia16322000812J at - 40 ℃570 - 640ABREX 600Japan15682058813J at  0 ℃550 - 650HARDOX 600Sweden16502000720J at - 40 ℃570 - 640XAR 600Germany17002000820J at - 20 ℃550.000All values marked in table is average value, Thus, it can be slightly different depands on the manufacturer environment

Abrasion Resistant Steel Plate Grade 500

Chemical CompositionGRADEBRANDORIGINChemical CompositionCSiMnCrMoBOTHERS(%)GR 500BISPLATE 500Australia0.320.350.401.200.300.002P 0.025ABREX 500Japan0.350.702.001.200.600.005P 0.015EVERHARD 500Japan0.350.551.600.800.500.004Ti 0.02RAEX 500Finland0.300.701.700.800.500.004Al 0.06XAR 500Germany0.280.801.501.000.500.005P 0.025HARDOX 500Sweden0.290.701.601.000.300.004Ni 0.50Mechaniacal PropertiesGRADEBRANDORIGINYeild Point(N/mm²)Tensile Strength(N/mm²)Elongation(%)Impact ValueHardness BeurinnelGR 500BISPLATE 500Australia140016401035J at + 20 ℃477 - 534ABREX 500Japan129416381837J at - 20 ℃450 - 550EVERHARD 500Japan129714491721J at  0 ℃450 - 550RAEX 500Finland12501600820J at - 30 ℃450 - 530XAR 500Germany125015001025J at - 20 ℃460 - 540HARDOX 500Sweden13001550830J at - 40 ℃470 - 530All values marked in table is average value, Thus, it can be slightly different depands on the manufacturer environment

Abrasion Resistant Steel Plate Grade 450

Chemical CompositionGRADEBRANDORIGINChemical CompositionCSiMnCrMoBOTHERS(%)GR 450BISPLATE 450Australia0.230.601.001.000.250.002P 0.025ABREX 450Japan0.230.702.001.200.600.005P 0.025RAEX 450Finland0.260.701.701.000.500.005P 0.025XAR 450Germany0.220.801.501.300.500.005P 0.025HARDOX 450Sweden0.260.701.601.400.500.005P 0.020Mechaniacal PropertiesGRADEBRANDORIGINYeild Point(N/mm²)Tensile Strength(N/mm²)Elongation(%)Impact ValueHardness BeurinnelGR 450BISPLATE 450Australia115014001225J at - 40 ℃425 - 475ABREX 450Japan11921469  410 - 490RAEX 450Finland12001450830J at - 40 ℃420 - 500XAR 450Germany120014001030J at - 40 ℃420 - 480HARDOX 450Sweden1100 - 13001400 - 1600340J at - 40 ℃425 - 475All values marked in table is average value, Thus, it can be slightly different depands on the manufacturer environment

Abrasion Resistant Steel Plate Grade 400

Chemical CompositionGRADEBRANDORIGINChemical CompositionCSiMnCrMoBOTHERS(%)GR 400BISPLATE 400Australia0.180.251.500.250.250.002P 0.025ABREX 400Japan0.210.702.001.200.600.005P 0.025EVERHARD 400Japan0.250.551.600.500.500.004Ti 0.02RAEX 400Finland0.240.701.701.000.500.004Al 0.06XAR 400Germany0.200.801.501.000.500.005P 0.025HARDOX 400Sweden0.180.701.601.000.250.004Ni 0.25Mechaniacal PropertiesGRADEBRANDORIGINYeild Point(N/mm²)Tensile Strength(N/mm²)Elongation(%)Impact ValueHardness BeurinnelGR 400BISPLATE 400Australia107013201455J at + 20 ℃370 - 430ABREX 400Japan107012362225J at - 20 ℃360 - 440EVERHARD 400Japan116313162021J at  0 ℃360 - 440RAEX 400Finland100012501020J at - 40 ℃380 - 450XAR 400Germany110013001235J at - 20 ℃360 - 440HARDOX 400Sweden100012501045J at - 40 ℃370 - 430All values marked in table is average value, Thus, it can be slightly different depands on the manufacturer environment

1